Catalysts 2012, 2, 171-190; doi:10.3390/catal2010171
catalystsISSN 2073-4344
www.mdpi.com/journal/catalysts
Article
Production of Bio-Hydrogenated Diesel by Hydrotreatment of High-Acid-Value Waste Cooking Oil over Ruthenium Catalyst Supported on Al-Polyoxocation-Pillared Montmorillonite
Yanyong Liu *, Rogelio Sotelo-Boyás †, Kazuhisa Murata, Tomoaki Minowa and Kinya Sakanishi
Biomass Technology Research Center, National Institute of Advanced Industrial Science and
Technology, AIST Tsukuba Center 5, 1-1-1 Higashi, Tsukuba, Ibaraki 305-8565, Japan;
E-Mails: rsotelob@gmail.com (R.S.-B.); kazu-murata@aist.go.jp (K.M.);
minowa.tom@aist.go.jp (T.M.); kinya-sakanishi@aist.go.jp (K.S.)
† Current address: Instituto Politecnico Nacional, Mexico ESIQIE, Mexico D.F. 07738, Mexico
* Author to whom correspondence should be addressed; E-Mail: yy.ryuu@aist.go.jp;
Tel.: +81-29-861-4826; Fax: +81-29-861-4776.
Received: 1 December 2011; in revised form: 19 January 2012 / Accepted: 7 February 2012 /
Published: 14 February 2012
Abstract: Waste cooking oil with a high-acid-value (28.7 mg-KOH/g-oil) was converted
to bio-hydrogenated diesel by a hydrotreatment process over supported Ru catalysts. The
standard reaction temperature, H2 pressure, liquid hourly space velocity (LHSV), and H2/oil
ratio were 350 °C, 2 MPa, 15.2 h–1, and 400 mL/mL, respectively. Both the free fatty acids
and the triglycerides in the waste cooking oil were deoxygenated at the same time to form
hydrocarbons in the hydrotreatment process. The predominant liquid hydrocarbon products
(98.9 wt%) were n-C18H38, n-C17H36, n-C16H34, and n-C15H32 when a Ru/SiO2 catalyst was
used. These long chain normal hydrocarbons had high melting points and gave the liquid
hydrocarbon product over Ru/SiO2 a high pour point of 20 °C. Ru/H-Y was not suitable for
producing diesel from waste cooking oil because it formed a large amount of C5–C10
gasoline-ranged paraffins on the strong acid sites of HY. When Al-polyoxocation-pillared
montmorillonite (Al13-Mont) was used as a support for the Ru catalyst, the pour point of
the liquid hydrocarbon product decreased to −15 °C with the conversion of a significant
amount of C15–C18 n-paraffins to iso-paraffins and light paraffins on the weak acid sites of
Al13-Mont. The liquid product over Ru/Al13-Mont can be expected to give a green diesel
for current diesel engines because its chemical composition and physical properties are
similar to those of commercial petro-diesel. A relatively large amount of H2 was consumed
OPEN ACCESS
Catalysts 2012, 2
172
in the hydrogenation of unsaturated C=C bonds and the deoxygenation of C=O bonds in
the hydrotreatment process. A sulfided Ni-Mo/Al13-Mont catalyst also produced
bio-hydrogenated diesel by the hydrotreatment process but it showed slow deactivation
during the reaction due to loss of sulfur. In contrast, Ru/Al13-Mont did not show catalyst
deactivation in the hydrotreatment of waste cooking oil after 72 h on-stream because the
waste cooking oil was not found to contain sulfur-containing compounds.
Keywords: bio-hydrogenated diesel; waste cooking oil; hydrotreatment; ruthenium;
Al-polyoxocation; pillared montmorillonite
1. Introduction
The increase of environmental concerns and the depletion of petroleum reserves have stimulated the
search for alternative renewable fuels to avoid climate change and energy shortage [1]. Bio-diesel,
which has been recognized as “green fuel”, is an important alternative fuel made from renewable
resources such as vegetable oil [2]. Although bio-diesel is a renewable fuel with environmental
benefits, the utilization of nonfood biomass is important from the viewpoint of food supply [3]. Waste
cooking oil is an important biomass resource without competition from food uses [4]. It is presumed
that 100–140 kt waste cooking oil from the household sector is discarded every year in Japan [5].
Recently the production of bio-diesel from waste cooking oil has been studied worldwide [6–9].
Fatty acid methyl ester (FAME) is the first generation bio-diesel and it is produced by the
transesterification of vegetable oil with methanol [10]. However, FAME has some shortcomings as a
fuel for the current diesel engines because both C=C bonds and C=O bonds remain in the molecules of
FAME [11]. The anti-oxidation ability of FAME is low due to unsaturated C=C double bonds, and the
flash point of FAME is high as FAME is less flammable than paraffins.
Bio-hydrogenated diesel (abbreviated as BHD) is called the second generation bio-diesel and it is
produced by the hydrotreatment of vegetable oil, instead of the transesterification of vegetable oil [12].
BHD is a paraffin mixture because all unsaturated C=C double bonds have been hydrogenated and all
oxygen atoms have been eliminated in the hydrotreatment process.
The waste cooking oil usually contains a high concentration of free fatty acids, which greatly
increase the cost in the production of FAME type bio-diesel. Base catalysts are highly active in the
transesterfication of triglycerides with methanol to produce FAME. However, base catalysts lose their
activity in the transesterfication of high-acid-value waste cooking oil as they react with free fatty acids
to form soap. Acid-catalyzed transesterification is much slower than base-catalyzed although some new
acid catalysts have been developed [6]. In general, a complex two-step process has to be used for the
FAME production from high-acid-value waste cooking oil: using acid catalysts to convert free fatty
acids in the first step and base catalysts to convert triglycerides in the second step. On the other hand,
the conversion of high-acid-value waste cooking oil to hydrocarbon type bio-diesel has an economical
advantage in that both free fatty acids and triglycerides are deoxygenated at the same time in a
one-step hydrotreatment process [13].
Catalysts 2012, 2
173
Although vegetable oil can be converted to a mixture of paraffins, cycloparaffins, and aromatic
hydrocarbons at high temperatures under high pressures even without a catalyst, a relatively large
amount of fatty acids usually remain in the products [14]. Solid acid catalysts (such as H-ZSM-5,
SO4/ZrO2, etc.) can convert vegetable oil to a mixture of gasoline, kerosene, light gas oil, gas oil, and
long chain residues by the hydrotreatment process [9,15]. Industrial FCC catalysts can convert
vegetable oil to gasoline distilled hydrocarbons in the FCC unit under the FCC conditions [16]. For
converting vegetable oil to bio-hydrogenated diesel (BHD), two types of effective catalysts have been
reported for the hydrotreatment process: noble metal catalysts (Pd, Pt, etc.) [17–21], and desulfurized
catalysts (sulfided Ni-Mo, Co-Mo, Ni-W, Co-W, etc.) [21–24].
The yield of C15–C18 n-paraffins usually has been stated in the literature for the hydrotreatment of
vegetable oil and it seems that the amount of C15–C18 n-paraffins determines the quality of BHD
fuel [18–22]. Actually, an extreme amount of C15–C18 n-paraffins give BHD a low fluidity and hinder
the use of BHD in current diesel engines. Any post-treatments in adapting BHD for current diesel
engines would increase the cost of BHD production. We think that the character of commercial normal
diesel from crude oil should be used as a goal for BHD because the current diesel engines have been
designed to use normal diesel as a fuel [23]. We have combined sulfided Ni-Mo and solid acids to
adjust the composition and properties of BHD in the hydrotreatment of vegetable oils [23,24].
However, the sulfided Ni-Mo catalyst slowly deactivated during the reaction because of sulfur
loss [24]. Ru has been reported as an effective noble metal catalyst for desulfurization [25]. Clays are
sorts of solid acids with a porous structure and unique acidity [26,27]. Pillaring large metal
polyoxocations (such as [AlO4Al12(OH)24(H2O)12]7+) into the interlayer region of clays (such as
montmorillonite) increases the surface area, pore size, and temperature stability of clay materials [27].
Al-polyoxocation-pillared montmorillonite has been reported as an excellent catalyst for producing
diesel distilled hydrocarbons from heavy vacuum gas oil and Fischer-Tropsch wax by the
hydrotreatment process [28,29].
In this study, we combined Ru with Al-polyoxocation-pillared montmorillonite to convert
high-acid-value waste cooking oil to BHD for current diesel engines by the hydrotreatment process, as
compared with other supports (SiO2 and H-Y zeolite) and metal catalyst (sulfided Ni-Mo).
2. Experimental Section
2.1. Materials
Waste vegetable cooking oil was obtained from a restaurant (served fried chicken) and used without
any purification. The standard reagents of fatty acids and triglycerides were purchased from
Sigma-Aldrich Chemical Company (St. Louis, MO, USA) and Tokyo Kasei Chemical Company
(Tokyo, Japan). Chemical reagents for synthesizing catalysts were purchased from Wako Pure
Chemical Industries Company (Tokyo, Japan).
Na-type montmorillonite (denoted as Na-Mont) is a natural clay mineral (Kunipia F) supplied by
Kunimine Industrial Company (Tokyo, Japan). The cation exchange capacity (CEC) was about
100 meq/100 g and the particle size was smaller than 2 μm in the Na-Mont sample. Na-Y zeolite
(SiO2/Al2O3 = 5.5; BET surface area: 382 m2·g–1) was purchased from Wako Pure Chemical Industries
Catalysts 2012, 2
174
Company (Tokyo, Japan). SiO2 support (BET surface area: 300 m2·g–1; average pore size: 10 nm) were
purchased from Fuji Silysia Chemical Company (Tokyo, Japan).
2.2. Catalysts
[AlO4Al12(OH)24(H2O)12]7+-pillared montmorillonite (denoted as Al13-Mont) was prepared by
ion-exchange [30,31]. The pillaring solution of [AlO4Al12(OH)24(H2O)12]7+ was prepared by the
dropwise addition of a solution of 0.2 M NaOH (2.4 g NaOH in 300 mL H2O) to a solution of 0.5 M
Al(NO3)3 (9.38 g Al(NO3)3·9H2O in 50 mL H2O) until a OH/Al molar ratio of 2.4. After standing at
room temperature for 24 h, 5 g Na-Mont was added to the pillaring solution. The final suspension was
stirred at room temperature for 12 h and a solid sample was obtained by filtration. The solid sample
was washed with distilled water three times, dried at 100 °C for 24 h, and calcined at 400 °C for 3 h.
H-Y was prepared from Na-Y by ion-exchange. Na-Y was stirred in an aqueous solution of
NH4NO3 (0.1 M) for 3 h and NH4-Y was then obtained after filtering from the water. The obtained
NH4-Y was dried at 100 °C for 24 h and calcined at 550 °C for 3 h to form H-Y.
Ru-supported catalysts (Ru/SiO2, Ru/H-Y, and Ru/Al13-Mont) were synthesized using a wet
impregnation method. The calcined solid support (SiO2, H-Y, or Al13-Mont) was impregnated with an
aqueous solution of RuCl3·nH2O (Ru: 40.6 wt%) with stirring. A solid sample was obtained after
evaporating the water by heating at 90 °C. The obtained solid sample was dried at 100 °C for 24 h and
calcined at 400 °C for 3 h. The designed Ru loading was 1.0 wt% in each catalyst because 5 g solid
support and 0.124 g RuCl3·nH2O (Ru: 40.6 wt%) in 50 mL water were used for the catalyst
preparation. The actual Ru loadings, which were measured by ICP elemental analysis, were similar to
the designed Ru loadings in various catalysts. Prior to the reaction, the catalysts were reduced in a H2
flow (flow rate: 60 mL·min–1) at 350 °C for 2 h.
Ni-Mo/Al13-Mont was synthesized as a reference catalyst using a co-impregnation method [31,32].
Al13-Mont support was added to a mixed aqueous solution of (NH4)6Mo7O24·4H2O and Ni(NO3)2·6H2O
to form a slurry. The slurry was stirred at 90 °C until formation of a solid sample by evaporating water.
The obtained solid sample was dried at 100 °C for 24 h and calcined at 400 °C for 3 h. The loadings of
MoO3 and NiO were 15 wt% and 3 wt% in Ni-Mo/Al13-Mont, respectively. Prior to the reaction, the
catalyst was sulfided and reduced in a mixed gas containing 10% H2S and 90% H2 (flow rate:
60 mL·min–1) at 400 °C for 10 h.
2.3. Characterization
The elemental composition of waste cooking oil was determined using an elemental analyzer
(CE instrument EA1110). The chemical composition of waste cooking oil was analyzed using an
Agilent 6890 N FID-GC with an Omnistar Q-mass. A HP-624 capillary column was used to separate
free fatty acids and an UA-TRG capillary column was used to separate triglycerides, diglycerides, and
monoglycerides. The density of waste cooking oil was determined at 20 °C using a density/specific
gravity meter (Kyoto Electronics DA-130N). The viscosity of waste cooking oil was determined at
40 °C using a vibro viscometer (A&D Co. Lim., Tokyo, Japan, SV-10). The acid value of waste
cooking oil was determined by an acid-base titration technique using a KOH aqueous solution (ASTM
D 664). The limit of detection was 0.1 mg-KOH/g-liquid in the measurement of the acid value.
Catalysts 2012, 2
175
Iodine values of the oils were measured by a titration technique using ICl and Na2S2O3 solutions
(ASTM D 1959).
Transmission electron microscopy (TEM) images were obtained using a JEOL JEM 2010FX
electron microscope equipped with a Hitachi/Keves H-8100/Delta IV EDS operating at 200 kV.
The ex situ treated samples were supported on Mo grids for the observations. The powder X-ray
diffraction (XRD) patterns were measured using a MAC Science MXP-18 diffractometer with Cu Kα
radiation operating at 40 kV and 50 mA. Temperature-programmed desorption of ammonia (NH3-TPD)
was carried out using a BELCAT-B automatic system equipped with a TCD and an Omnistar Q-mass.
A part of the 0.05 g sample was pretreated at 400 °C for 1 h in a He flow with a flow rate of
50 mL·min–1. After the temperature was decreased to 100 °C, ammonia was adsorbed onto the
sample’s surface, followed by evacuation for 1 h at 100 °C to eliminate the weakly adsorbed ammonia.
Then, NH3-TPD was recorded from 100 to 600 °C with a rate of 8 °C·min–1.
2.4. Reaction
A high-pressure continuous flow fixed-bed reactor was used for the experimental investigation.
Figure 1 shows the reaction system used in this study. A stainless steel tubular reactor (i.d.: 1 cm;
length: 50 cm) was used for loading the catalyst and a furnace was used for heating the tubular reactor.
The waste cooking oil was forced into the reactor at a constant rate by a JP-H type high-pressured
micro-feeder (Furue Science Company). Meanwhile, a mixed gas containing 90% H2 and 10% Ar
(using as an internal standard) was introduced into the reactor from a high-pressure H2 cylinder and the
flow rate was controlled by a mass flow controller. A cooling trap (put in ice-water) was set between
the reactor exit and the back-pressure regulator to collect liquid products.
Figure 1. Reaction system used in this study. (1) H2 cylinder; (2) pressure regulator;
(3) mass flow controller; (4) tank of waste cooking oil; (5) high-pressured micro-feeder;
(6) stainless steel tubular reactor; (7) catalyst layer; (8) furnace; (9) cold trap; (10) tank of
ice-water; (11) outlet of liquid product; (12) back-pressure regulator; (13) on-line GCs.
Catalysts 2012, 2
176
The catalyst was loaded onto an iron plate with many small holes in the center of the tubular reactor.
The pressure in the reaction system was controlled by a back-pressure regulator. The reaction
temperature was controlled by a temperature-controller equipped with a thermocouple. The top of the
thermocouple was in contact with the surface of the catalyst layer to determine the reaction
temperature. The standard reaction conditions were listed as follows: catalyst amount: 1 g (mixed with
quartz sand to 5 mL in total volume); reaction temperature: 350 °C; H2 pressure: 2 MPa; LHSV (liquid
hourly space velocity, which is a ratio of the volume of liquid feed to the volume of catalyst and quartz
sand): 15.2 h–1; ratio of H2 to oil in feed: 400 mL/mL, in which the H2 volume was described in the
conditions of standard temperature and pressure (STP).
2.5. Analyses
The gas products were continuously analyzed by an on-line GC system during the reaction. Inorganic
gases (H2, Ar, CO and CO2) were analyzed using a Shimadzu 8A TCD-GC equipped with MS-5A and
Porapak-Q columns. Gaseous hydrocarbons (C1–C4) were analyzed using an Agilent 6890 N FID-GC
equipped with a RT-QPLOT capillary column. The factors of various gases were obtained using a
standard mixed gas (with known concentration for each component) from a cylinder.
The liquid products were taken out from the cooling trap after the reaction. After removing the
water layer in the bottom using a separation funnel, a certain amount of 1-methylnaphthalene was
added to the oil phase as an internal standard. The oil phase was then analyzed by an Agilent 6890 N
FID-GC equipped with three capillary columns: a UA-DX30 capillary column for analyzing
C5+ hydrocarbons, a HP-624 capillary column for analyzing fatty acids, and a UA-TRG capillary
column for analyzing triglycerides, diglycerides, and monoglycerides.
The yields of C1–C4 hydrocarbons, CO and CO2 in the gas products were calculated using
Ar as internal standard. The yields of organic compounds in the liquid products were calculated using
1-methylnaphthalene as internal standard. The yield of water was calculated from the weights of
formed water and introduced oil. The carbon mass balance had an error <5% over each catalyst.
3. Results and Discussion
3.1. Characterization of Catalysts
Table 1 summarizes the basic characteristics of the Na-Mont and Al13-Mont before and after
calcination. The value of the basal plane reflection (d001) at the lowest angle in the XRD pattern
includes the thickness of a host layer and the gallery height of an interlayer region [26,33]. Because the
interlayer cations support the montmorillonite layers, any alternations of interlayer cations certainly
cause changes of the d001 basal plane in the XRD pattern. The thickness of the host layer is about 9.3 Å
for montmorillonite compounds [26,27]. As shown in Table 1, the d001 basal plane at 25 °C in the XRD
pattern increased from 12.4 Å to 19.2 Å after Al13 polyoxocation pillaring. After subtracting the
thickness of the host layer (9.3 Å) from the d001 spacing, Na-Mont had a gallery height of 3.1 Å and
Al13-Mont had a gallery height of 9.9 Å. The Al13 polyoxocations were successfully introduced into
the interlayer region in Al13-Mont because the gallery height coincided with the size of Al13
Catalysts 2012, 2
177
polyoxocation [26,27]. The d001 value of Na-Mont decreased to 10.6 Å after calcination at 300 °C for
3 h and could not be observed after calcination at 500 °C for 3 h.
Table 1. Basic characteristics of raw montmorillonite and its Al13-pillared derivative.
Sample Tcalcination (°C) d001 (Å) BET (m2/g) Total Vp (cm3/g) Micro Vp (cm3/g)
Na-Mont 25 12.4 82 0.079 0.004 300 10.6 38 0.068 0.005 400 10.5 29 0.065 0.004 500 – 26 0.063 0.003
Al13-Mont 25 19.2 156 0.150 0.078 300 18.5 237 0.170 0.111 400 18.5 270 0.180 0.122 500 17.9 189 0.152 0.103
As shown in Table 1, the BET surface area of Al13-Mont was significantly higher than that of its
precursor Na-Mont at 25 °C. The height between two clay layers in Na-Mont was only 3.1 Å (from
XRD results) and many water molecules existed in the interlayer region at 25 °C. Hence, the interior of
the interlayer region in Na-Mont was difficult to utilize for adsorbing N2 molecules in the BET
measurement. On the other hand, the gallery height of Al13-Mont increased to 9.9 Å (from XRD
results) and thus N2 molecules easily enter the interlayer region, which caused a significant increase of
BET surface area of Al13-Mont at 25 °C. Moreover, the BET surface area of Na-Mont decreased to
38 m2/g after calcination at 300 °C for 3 h due to the collapse of the layered structure. On the other
hand, the d001 value of Al13-Mont slightly decreased to 18.5 Å upon calcination at 300 °C due to the
dehydration of Al13 polyoxocation. The BET surface area of Al13-Mont increased with increasing
calcination temperature up to 400 °C, followed by a decrease of surface area upon calcination at
500 °C. Hence, Al13-Mont retained the layered structures after calcination at 400 °C owing to the
robust polyoxocation pillars but were partly destroyed upon calcination at 500 °C. As for the pore size
of a montmorillonite compound, it is defined not only by the interlayer distance (between two clay
layers) but also by the lateral distance (between two interlayer pillars). The micropore (pores diameter
<20 Å) volume of Na-Mont was very low (about 0.004 cm3/g). On the other hand, Al13-Mont is a
misroporous material because its micropore volume is relatively large. Both the total pore volume and
the micropore volume of Al13-Mont increased with increasing calcination temperature up to 400 °C and
decreased upon calcination at 500 °C due to partial destruction of the layered structure. Therefore, the
calcination temperature for Al13-Mont-containing catalysts was set at 400 °C in this study.
Figure 2 shows the TEM image of Ru/Al13-Mont (Ru loading: 1 wt%) catalyst after reduction in a
H2 flow at 300 °C for 2 h. The layered structure of montmorillonite support could be observed from the
TEM image. The gallery height was about 1 nm and this value coincided with the size of Al13
polyoxocation. The black Ru particles could be observed on the surface of the montmorillonite support.
The Ru particles did not enter into the interlayer region of montmorillonite in Ru/Al13-Mont. The
distribution of Ru particles was relatively uniform and the particle size of Ru was about 3–5 nm.
Catalysts 2012, 2
178
Figure 2. TEM image of Ru/Al13-Mont (Ru loading: 1 wt%) catalyst after reduction.
Figure 3. NH3-TPD profiles of various solid supports.
Figure 3 shows the NH3-TPD of various solid supports used in this study. NH3-TPD is a powerful
tool for estimating the acidic property of a solid surface. The adsorbed NH3 molecules desorbed from
weak acid sites at low temperatures and desorbed from strong acid sites at high temperatures.
As shown in Figure 3, SiO2 did not show an obvious peak in the NH3-TPD profile, indicating that SiO2
Catalysts 2012, 2
179
did not have acid sites on the surface. Al13-Mont had acid sites on the surface area because its
NH3-TPD showed a peak with a maximum value at 170 °C. Because H-Y showed two peaks at about
180 and 350 °C, H-Y had two types of acid sites (weak acid sites and strong acid sites) on the surfaces.
The peak at the maximum temperature in the NH3-TPD profile corresponds to the strongest acid sites
on the solid surface. The nature of a solid acid catalyst is mainly determined by the strongest acid sites
on the surface. According to the peak position at the maximum temperature in the NH3-TPD profiles,
the acidic strength of various supports was in an order of H-Y > Al13-Mont > SiO2 (no acidity).
3.2. Composition and Property of Waste Cooking Oil
Table 2 shows the composition and property of the waste cooking oil used in this study.
Table 2. Composition and property of the waste cooking oil used in this study.
Elemental composition Weight percent (wt%)
C 77.91
H 11.69
N 0.04
S 0
O 10.36
Chemical composition Content (g/100 g-oil)
Triglyceride 79.1
Diglyceride 1.8
Monoglycerid 2.2
Free fatty acid 16.9
Others Acid value
(mg-KOH/g-oil) 28.7
Iodine value (g-I2/100 g-oil)
88.6
Viscosity (mPa/s)
57.8
Density (g/mL)
0.92
The elemental composition of the waste cooking oil was determined using an elemental analyzer
(CE instrument EA1110). The difference from 100% was taken as the content of oxygen. As shown in
Table 2, the amount of N was very small (0.04 wt%) and S could not be observed in the waste cooking
oil. In general, vegetable oils do not contain sulfur-containing compounds. Therefore, the bio-diesels
produced from vegetable oils are regarded as environmentally benign green fuels. Concurrently, the
development of catalysts for the hydrotreatment of vegetable oils (without S) is different from those
for the hydrotreatment of fossil fuels with sulfur-containing compounds.
The chemical components in the waste cooking oil were confirmed by GC-MS results and standard
reagents. The content of free fatty acids was very high (16.9 g/100 g-oil) in the waste cooking oil.
It seems that the waste cooking oil can not be used as a straight vegetable oil (SVO) just after filtration
because the free fatty acids are corrosive to diesel engines. For the FAME production, base catalysts
lose their activity in the transesterfication of cooking vegetable oil because of soap formation from free
fatty acids and basic catalysts. A complex two-step process has to be used for the FAME production
(using acid catalyst to convert free fatty acids in the first step and using base catalyst to convert
triglycerides in the second step) which must increase the cost of the FAME production. Therefore, the
one-step hydrotreatment process is suitable for the commercial production of BHD from waste
cooking oil.
As for the physical properties, the acid value of the waste cooking oil was very high
(28.7 mg-KOH/g-oil) because it contained a large amount of free fatty acids. The iodine value of the
waste cooking oil was 88.6 g-I2/100 g-oil, indicating that the waste cooking oil contained many C=C
unsaturated bonds. The viscosity at 30 °C was 57.8 mPa/s and the density at 25 °C was 0.92 g/mL for
the waste cooking oil. The viscosity was too high to use the waste cooking oil in current diesel engines.
Catalysts 2012, 2
180
Table 3 shows the species of free fatty acid (FFA) in the waste cooking oil used in this study. The
formula of each fatty acid was confirmed by GC-MS (HP-624 capillary column) results with standard
reagents. The content of each fatty acid shown in Table 3 was expressed as its weight in 100 g free
fatty acid, while 100 g waste cooking oil contained 16.9 g free fatty acid (Table 2). The main free fatty
acids in the waste cooking oil were palmitic acid (6.6%), stearic acid (7.8%), oleic acid (53.6%),
linoleic acid (16.4%), and linolenic acid (14.3%). The unsaturated fatty acids (with C=C double bond)
included palmitoleic, oleic, linoleic, linolenic, and eicosenoic acids, while the saturated fatty acids
(without C=C double bond) included palmitic and stearic acids. By calculating using these data, the
unsaturated fatty acids occupied 85.6% and the saturated fatty acids occupied 14.4% in total free fatty
acids of the waste cooking oil. All free fatty acids in the waste cooking oil had even carbon numbers
(16, 18, and 20) in the carbon chains. The fatty acids with sixteen carbons in the carbon chain
(so-called C16-acids, including palmitic and palmitoleic acids) occupied 6.8%, the fatty acids with
eighteen carbons in the carbon chain (so-called C18-acids, including stearic, oleic, linoleic and
linolenic acids) occupied 92.1%, and the fatty acids with twenty carbons in the carbon chain (so-called
C20-acids, including eicosenoic acid) occupied 1.1% in total free fatty acids of the waste cooking oil.
Table 3. Species of free fatty acid (FFA) in the waste cooking oil used in this study.
Formula Name Structure a Content (g/100 g-FFA) C16H32O2 Palmitic C16:0 6.6 C16H30O2 Palmitoleic C16:1 0.2 C18H36O2 Stearic C18:0 7.8 C18H34O2 Oleic C18:1 53.6 C18H32O2 Linoleic C18:2 16.4 C18H30O2 Linolenic C18:3 14.3 C20H38O2 Eicosenoic C20:1 1.1
a Cx:y, where x is the number of carbon atoms and y is the number of C=C double bonds.
3.3. Hydrotreatment of Waste Cooking Oil over Ru-Supported Catalysts
Table 4 shows the product yields over various catalysts in the hydrotreatment of waste cooking oil.
The conversion was 100% and did not decrease after reaction for 10 h over each catalyst because
triglycerides and fatty acid acids could not be detected in the products. The yield of fuel gas (C1 + C2)
was very low (<1.0 wt%) over each catalyst. The yield of liquid fuel (C5+ hydrocarbons) was in a
narrow range of 82.1–84.0 wt% and the yield of LPG (C3 + C4) was in a narrow range of
4.8–5.6 wt% over each catalyst. Both liquid hydrocarbons (C5+) and LPG (C3 + C4) can be used as fuels
for automobiles. Water (yield: 7.7–8.0 wt%) and COx (including CO and CO2, yield: 3.2–3.4 wt%) were
also formed in the hydrotreatment process over each catalyst. Because propane is formed after all C=O
bonds in triglycerides are broken during the hydrotreatment process, propane occupied more than
90 wt% in the formed LPG (C3 + C4) over each catalyst.
Catalysts 2012, 2
181
Table 4. Product yields over various catalysts in the hydrotreatment of waste cooking oil a.
Catalyst C1 + C2 C3 + C4 C5+ COx H2O Ru/SiO2 0.2 4.8 84.0 3.3 7.7
Ru/Al13-Mont 0.4 5.0 83.6 3.2 7.8 Ru/H-Y 0.9 5.6 82.1 3.4 8.0
a Reaction temperature: 350 °C; H2 pressure: 2 MPa; H2/oil in feed: 400 mL/mL; LHSV: 15.2 h–1.
The waste cooking oil contained triglycerides, diglycerides, monoglycerides, and free fatty acids
(Table 2). The hydrotreatment process on the Ru sites contained two steps: hydrogenation and
deoxygenation. In the first step, all unsaturated C=C bonds in the triglycerides, diglycerides,
monoglycerides, and free fatty acids were saturated on their carbon chains by the hydrogenation on the
Ru sites. In the second step, the saturated triglycerides decomposed by scission of the C=O bonds,
leading to the formation of diglycerides, monoglycerides, and carboxylic acids (fatty acids) in order,
and the carboxylic acids then underwent deoxygenation on the Ru sites to form hydrocarbons.
Therefore, the key step in the hydrotreatment of waste cooking oil is the deoxygenation of saturated
fatty acids.
The deoxygenation of saturated fatty acids (such as stearic acid C17H35COOH) contains three
parallel reactions: reduction, decarbonylation, and decarboxylation [22].
C17H35COOH + 3H2 = C18H38 + 2H2O (Reduction) (Reaction 1)
C17H35COOH + H2 = C17H36 + CO + H2O (Decarbonylation) (Reaction 2)
C17H35COOH = C17H36 + CO2 (Decarboxylation) (Reaction 3)
As shown in Reactions 1–3, for a fatty acid with an even carbon number, the reduction produces a
normal paraffin with an even carbon number plus water; the decarbonylation produces a normal paraffin
with an odd carbon number plus water and CO; and the decarboxylation produces a normal paraffin
with an odd carbon number plus CO2. Both the decarbonylation and the decarboxylation occurred
during the reaction because both CO and CO2 were detected in the gas product over each catalyst.
As shown in Table 4, the three catalysts had similar yields of C5+ liquid hydrocarbons (ranging from
82.1 to 84.0 wt%) from the hydrotreatment of waste cooking oil. However, it is necessary to investigate
whether these liquid hydrocarbons are suitable for use as a diesel fuel in current diesel engines.
Figure 4 shows the FID-GC charts (UA-DX capillary column) of liquid hydrocarbons formed from
the hydrotreatment of waste cooking oil over various catalysts. Ru/SiO2 formed n-C18H38, n-C17H36,
n-C16H34, and n-C15H32 as the main products and the amounts of iso-paraffins and light paraffins
(≤C14) were very low. According to Reactions 1–3, n-C16H34 and n-C18H38 were formed by the reduction
of palmitic acid and stearic acid, and n-C15H32 and n-C17H36 were formed by the decarbonylation and
decarboxylation of palmitic acid and stearic acid, respectively. In order to adjust the chemical
composition of the liquid hydrocarbon product, we supported Ru catalyst on solid acids (H-Y,
Al13-Mont) for the isomerization/cracking of C15H32–C18H38 n-paraffins as the third step after the
hydrogenation and deoxygenation steps. The isomerization/cracking of n-paraffins over bifunctional
catalysts containing metal and solid acid is very important for improving the properties of liquid
hydrocarbon fuels [34–37]. The reaction proceeds via carbenium ion intermediates formed on the solid
acid sites. The acidic strength of the solid acid determines the activity of the bifunctional catalysts
Catalysts 2012, 2
182
when the same metal is used in the isomerization/cracking of n-paraffins. Because the acidic strength
of various supports was in the order of H-Y > Al13-Mont > SiO2 (Figure 3), Ru/H-Y formed a large
amount of light hydrocarbons (≤C14) and Ru/Al13-Mont formed a significant amount of light
hydrocarbons (≤C14) (Figure 4).
Figure 4. FID-GC charts of liquid hydrocarbons formed from the hydrotreatment of waste
cooking oil over various catalysts (reaction conditions: same as those in Table 4).
Table 5. Composition and property of the liquid hydrocarbons (C5+) formed from the
hydrotreatment of waste cooking oil over various catalysts a.
Catalyst
Composition (wt%) Property
C5–C10 C11–C20 C20+ Iso/n ratio
Pour Point (°C)
Density at 25 °C (g/mL)
Viscosity at 30 °C (mPa/s)
Ru/SiO2 0.9 98.9 0.2 0.08 20 0.79 8.01 Ru/Al13-Mont 9.1 89.8 1.1 0.22 −15 0.78 3.96 Ru/H-Y 42.8 56.5 0.7 0.43 — b 0.77 2.08 Normal diesel c 8.2 88.1 3.7 0.28 −15 0.82 3.69
a Reaction temperature: 350 °C; H2 pressure: 2 MPa; H2/oil in feed: 400 mL/mL; LHSV: 15.2 h−1; b Lower
than −25 °C; c A commercial diesel bought from a petrol station.
Table 5 shows the composition and property of the liquid hydrocarbons (C5+) formed from the
hydrotreatment of waste cooking oil over various catalysts. Although the liquid hydrocarbons formed
over Ru/SiO2 contained the largest amount of C11–C20 diesel-distillate (98.9 wt%) with the lowest
Catalysts 2012, 2
183
iso/n ratio (0.08) among various catalysts, the pour point of the product was too high (20 °C) to use as
a diesel fuel. Ru/H-Y was also not suitable for producing BHD from the waste cooking oil because it
formed a large amount of C5–C10 gasoline-distillate (42.8 wt%) on the strong acid sites. Ru/Al13-Mont
produced a liquid hydrocarbon product with a pour point of −15 °C with an iso/n ratio of 0.22.
The melting points of n-C18H38, n-C17H36, n-C16H34, and n-C15H32 are 28, 22, 18, and 10 °C,
respectively. A predominant amount of C15–C18 n-paraffins gave a high pour point (20 °C) for the
liquid hydrocarbon product over Ru-Mo/SiO2 (Table 5). It is necessary to decrease the pour point of
the product over Ru/SiO2 in order to use it in the current diesel engines. Iso-paraffins and light paraffins
have relatively low melting points (for example, 2-methyl-heptadecane: 5 °C; 3-methyl-heptadecane:
−6 °C; 2-methyl-hexadecane: 5 °C; 2-methyl-pentadecane: −11 °C; 3-methyl-pentadecane: −22 °C;
2-methyl-tetradecane: −8 °C; 3-methyl-tetradecane: −36 °C; n-C11H24: −25 °C). Hence, we supported
Ru on solid acids (Al13-Mont and H-Y) to improve the fluidity of the liquid hydrocarbon product from
the hydrotreatment of waste oil by the isomerization/cracking of C15H32–C18H38 n-paraffins.
The hydrocarbons ranging from C11 to C20 are called diesel-distillate and the hydrocarbons ranging
from C5 to C10 are called gasoline-distillate. However, the commercial normal diesel bought from a
petrol station actually contains 8.2 wt% of C5–C10 gasoline-distillate to improve the fluidity (Table 5).
The viscosity of the liquid hydrocarbon product over Ru/Al13-Mont was 3.96 mPa/s, which was quite
similar to that of the normal diesel (3.69 mPa/s). The density of the normal diesel was relatively large
(0.82 g/mL), probably because the normal diesel contained some heavy additives. On the whole, both
composition and pour point of the liquid hydrocarbon product over Ru/Al13-Mont were quite similar to
those of the normal diesel bought from a petrol station. Because the current diesel engines have been
designed to use normal diesel as a fuel, we think that the product over Ru/Al13-Mont (with similar
composition and property to normal diesel) is better than the product over Ru/SiO2 (with 98.9 wt%
C11–C20 diesel-distillate and high pour point) as a diesel fuel for current diesel engines. As a result,
because Al13-Mont had a significant acidic strength, the liquid hydrocarbon product in the
hydrotreatment of waste cooking oil over Ru/Al13-Mont can be expected to give a green BHD fuel
directly usable in the current diesel engines without any post-treatment processes (such as distillation,
upgrading, etc.).
3.4. Influence of Reaction Conditions in the Hydrotreatment of Waste Cooking Oil over Ru/Al13-Mont
Because the molecules of triglycerides and free fatty acids in the waste cooking oil contained many
unsaturated C=C bonds and C=O bonds, the H2 amount and H2 pressure are important reaction
conditions for the hydrotreatment of waste cooking oil to produce saturated hydrocarbons.
Figure 5 shows the effect of H2/oil ratio in the hydrotreatment of waste cooking oil over
Ru/Al13-Mont. The H2/oil was a ratio of H2 feed rate to liquid (waste cooking oil) feed rate during the
reaction and the H2 volume was described in conditions of standard temperature and pressure (STP). A
low H2/oil is desirable for producing BHD for commercialization as it is favorable to reduce the cost of
production. However, the peaks of fatty acids could be detected in the GC chart at a H2/oil ratio of 300
(Figure 5). Thus a H2/oil ratio of 400 was necessary for the hydrotreatment of waste cooking oil over
Ru/All3-Mont. As shown in Reactions 1–3, the deoxygenation of fatty acids contained three parallel
reactions: reduction, decarbonylation and decarboxylation. The reduction does not produce COx, while
Catalysts 2012, 2
184
both the decarbonylation and the decarboxylation produces COx and thus one C in the carbon chain is
lost. Thus from the deoxygenation of C16-acids and C18-acids, the reduction produces n-C16H34 and
n-C18H38, and the decarbonylation and decarboxylation produce n-C15H32 and n-C17H36. Moreover, the
reduction is favorable under a large H2/oil ratio because it consumes more H2 molecules than the
decarbonylation and decarboxylation (Reactions 1–3). Hence, the ratios of C18/C17 and C16/C15 in
products over Ru/Al13-Mont decreased with decreasing H2/oil ratio from 500 to 300 (Figure 5).
Figure 5. FID-GC charts of liquid products in the hydrotreatment of waste cooking oil over
Ru/Al13-Mont under various H2/oil ratios (T: 350 °C; H2 pressure: 2 MPa; liquid hourly
space velocity (LHSV): 15.2 h–1).
Figure 6. FID-GC charts of liquid products in the hydrotreatment of waste cooking oil
over Ru/Al13-Mont under various H2 pressures (T: 350 °C; H2/oil: 400; LHSV: 15.2 h–1).
Catalysts 2012, 2
185
Figure 6 shows the effect of H2 pressure in the hydrotreatment of waste cooking oil over
Ru/Al13-Mont. A low H2 pressure is desirable for producing BHD in commercialization because it is
favorable to reduce the investment in plant and equipment. The peaks of fatty acids could not be
observed in the GC chart under 2 MPa of H2 pressure but could be detected in the GC chart under
1 MPa of H2 pressure. Hence, a H2 pressure of 2 MPa was necessary for the hydrotreatment of waste
cooking oil over Ru/All3-Mont. As shown in Reactions 1–3, the reduction (for producing n-C18H38 and
n-C16H34) is favorable under a high H2 pressure in comparison with the decarbonylation and
decarboxylation (for producing n-C17H36 and n-C15H32). Thus the ratios of C18/C17 and C16/C15 in
products over Ru/Al13-Mont decreased with decreasing H2 pressure.
Figure 7 shows the effect of reaction temperature in the hydrotreatment of waste cooking oil over
Ru/Al13-Mont. When the reaction was carried out at a low reaction temperature of 300 °C, the peaks of
fatty acids were observed in the GC chart. This means that the deoxygenation of waste cooking oil was
not enough at 300 °C. The peaks of fatty acids could not be observed in GC charts at high reaction
temperatures of 350 °C and 400 °C. Although n-C18H38, n-C17H36, n-C16H34, and n-C15H32 are the main
products over all three catalysts, the amount of light hydrocarbons (≤C14) formed remarkably increased
when the reaction temperature increased from 300 to 400 °C. We think the cracking of C15H32–C18H38
nomal paraffins caused the increase of light hydrocarbons (≤C14) at high reaction temperatures. Hence,
the reaction temperature also can be used to adjust the composition and property of the BHD product.
Because the amount of C5–C10 gasoline-distillate hydrocarbons was too much at 400 °C, the most
suitable reaction temperature was found to be 350 °C in the hydrotreatment of waste cooking oil.
Figure 7. FID-GC charts of liquid products in the hydrotreatment of waste cooking oil
over Ru/Al13-Mont at various reaction temperatures (H2 pressure: 2 MPa; H2/oil: 400;
LHSV: 15.2 h–1).
The goal of this study is to produce green BHD fuel for use in current diesel engines without any
post-treatment. The liquid organic phase in the product should not contain any fatty acids because they
Catalysts 2012, 2
186
are corrosive to engines. Moreover, a significant amount of C5–C10 gasoline-distillate (similar to the
amount in commercial normal diesel) should be contained in order to adjust the physical properties of
BHD fuel to fit current diesel engines. Hence, we chose a H2/oil ratio of 400 mL/mL, a H2 pressure of
2 MPa, and a reaction temperature of 350 °C as the standard reaction conditions in this study.
3.5. Deactivation of Ru/Al13-Mont and Sulfided Ni-Mo/Al13-Mont Catalysts
Figure 8 shows the time sequences in the hydrotreatment of waste cooking oil over Ru/Al13-Mont
and sulfided Ni-Mo/Al13-Mont. Ru/Al13-Mont showed an initial C5+ hydrocarbons yield of 83.6% and
it did not decrease after reaction for 72 h. This indicated that Ru/Al13-Mont had a high catalytic
stability for the hydrotreatment of waste cooking oil. In contrast, sulfided Ni-Mo/Al13-Mont showed an
initial C5+ hydrocarbons yield of 83.5% but it slowly decreased to 76.8% after reaction for 72 h.
Ni-Mo/Al13-Mont was sulfided by 10% H2S (in 90% H2) at 400 °C prior to the reaction and a Ni-Mo-S
phase was formed as the active phase for the hydrotreatment of waste cooking oil. The sulfur component
in sulfided Ni-Mo/Al13-Mont was lost slowly during the reaction [24]. Because the waste cooking oil
used in this study did not contain a sulfur component (Table 2), the loss of sulfur could not be
supplemented by the feedstock. As shown in Figure 8, the speed of deactivation was slow in the first
10 h and became fast after reaction for 10 h over sulfided Ni-Mo/Al13-Mont. The loss of sulfur caused
the collapse of the Ni-Mo-S active phase in sulfided Ni-Mo/Al13-Mont. As for Ru/Al13-Mont, it could
maintain activity during the reaction because the feedstock did not contain any sulfur poisons.
Figure 8. Time courses in the hydrotreatment of waste cooking oil over Ru/Al13-Mont (●)
and sulfided Ni-Mo/Al13-Mont (■) (reaction conditions: same as those in Table 4).
Figure 9 shows the time sequences in the hydrotreatment of waste cooking oil containing 10 ppm
dimethyl disulfide (DMDS) over Ru/Al13-Mont and sulfided Ni-Mo/Al13-Mont. A large number of
liquid fuels produced from crude oil, coal, and biomass contain sulfur compounds. We added 10 ppm
Catalysts 2012, 2
187
DMDS as a standard sulfur compound in the waste cooking oil to check the influence of sulfur on
Ru/Al13-Mont and sulfided Ni-Mo/Al13-Mont catalysts. As shown in Figure 9, Ru/Al13-Mont showed
an initial C5+ hydrocarbons yield of 83.6% and it decreased to 75.8% after reaction for 72 h for the
hydrotreatment of waste cooking oil containing 10 ppm DMDS. Because S rapidly reacted with the Ru
atoms to form an inactive RuS phase on the catalyst surface, the speed of deactivation over
Ru/Al13-Mont was fast in the first 10 h and then became slow. In contrast, sulfided Ni-Mo/Al13-Mont
showed an initial C5+ hydrocarbons yield of 83.5% and it did not decrease after reaction for 72 h. The
sulfur compound (DMDS) in the feed waste cooking oil supplemented the loss of sulfur from the
surface of sulfided Ni-Mo/Al13-Mont catalyst. The structure the Ni-Mo-S active phase remained during
the reaction and maintained the catalytic activity of sulfided Ni-Mo/Al13-Mont. Some researchers have
carried out the hydrotreatment of vegetable oil (not containing S) mixed with heavy vacuum oil
(containing S) over Ni-Mo catalysts in order to maintain the catalyst stability [22]. Hence, in the
hydrotreatment process, noble catalysts (Ru, Pt, Pd, etc.) are suitable for the feedstock without a
S component (such as vegetable oils, F-T waxes, etc.), and desulfurizated catalysts (sulfided Ni-Mo,
Co-Mo, Ni-W, Co-W, etc.) are suitable for the feedstock containing S compounds (such as heavy oil,
bio oil, etc.).
Figure 9. Time sequences in the hydrotreatment of waste cooking oil containing 10 ppm
DMDS over Ru/Al13-Mont (●) and sulfided Ni-Mo/Al13-Mont (■) (reaction conditions:
same as those in Table 4).
4. Conclusions
The waste cooking oil containing 16.9 wt% free fatty acids was converted to mixed paraffins over
Ru-supported catalysts by a one-step hydrotreatment process in which both free fatty acids and
triglycerides were deoxygenated at the same time. The fluidity of the liquid hydrocarbon product over
Ru/SiO2 was poor because of a predominant amount of C15H32–C18H38 n-paraffins. By supporting Ru
Catalysts 2012, 2
188
on acidic Al13-Mont, both the chemical composition and the pour point of the liquid hydrocarbon
product became quite similar to those of a commercial normal diesel. Ru/Al13-Mont acted as a
multifunctional catalyst enabling hydrogenation, deoxidization, and isomerization/cracking for the
hydrotreatment of waste cooking oil. The lowest H2/oil ratio was 400 and the lowest H2 pressure was
2 MPa to convert the waste cooking oil to saturated hydrocarbons over Ru/Al13-Mont as the waste
cooking oil contained many unsaturated C=C bonds and C=O bonds. Ru/Al13-Mont did not deactivate
after reaction for 72 h because the waste cooking oil did not contain S compounds as poisons for Ru.
References
1. Fernando, S.; Adhikari, S.; Chandrapal, C.; Murali, N. Biorefineries: Current status, challenges,
and future direction. Energy Fuel 2006, 20, 1727–1737.
2. Sharma, Y.C.; Singh, B.; Upadhyay, S.N. Advancements in development and characterization of
biodiesel: A review. Fuel 2008, 87, 2355–2373.
3. Pinzi, S.; Garcia, L.; Lopez-Gimenez, F.J.; Luque de Castro, M.D.; Dorado, G.; Dorado, M.P. The
ideal vegetable oil-based biodiesel composition: A review of social, economical and technical
implications. Energy Fuel 2009, 23, 2325–2341.
4. Kulkarni, M.G.; Dalai, A.K. Waste cooking oil—An economical source for biodiesel: A review.
Ind. Eng. Chem. Res. 2006, 45, 2901–2913.
5. Japanese government biomass policies: Major source of introduction of biofuel. Report on
Promotion of Eco-Fuel for Transportation; Japanese Government: Tokyo, Japan, 2006.
6. Cao, F.; Chen, Y.; Zhai, F.; Li, J.; Wang, J.; Wang, X.; Wang, S.; Zhu, W. Biodiesel production
from high acid value waste frying oil catalyzed by superacid heteropolyacid. Biotechnol. Bioeng.
2008, 101, 93–100.
7. Toba, M.; Abe, Y.; Kuramochi, H.; Osako, M.; Mochizuki, T.; Yoshimura, Y. Hydrodeoxygenation
of waste vegetable oil over sulfide catalysts. Catal. Today 2011, 164, 533–537.
8. Xu, J.; Xiao, G.; Zhou, Y.; Jiang, J. Production of biofuels from high-acid-value waste oils.
Energy Fuel 2011, 25, 4638–4642.
9. Charusiri, W.; Vitidsant, T. Kinetic study of used vegetable oil to liquid fuels over sulfated zirconia.
Energy Fuel 2005, 19, 1783–1789.
10. Ma, F.; Hanna, M.M. Biodiesel production: A review. Bioresour. Technol. 1999, 70, 1–15.
11. Sharma, Y.C.; Singh, B.; Upadhyay, S.N. Advancements in development and characterization of
biodiesel: A review. Fuel 2008, 87, 2355–2373.
12. Kalnes, T.; Markery, T.; Shonnard, D.R. Green diesel: A second generation biofuel. Int. J. Chem.
React. Eng. 2007, 5, A48.
13. Guzman, A.; Torres, J.E.; Prada, L.P.; Nunez, M.L. Hydropressing of crude palm oil at pilot plant
scale. Catal. Today 2010, 156, 38–43.
14. Li, L.; Coppola, E.; Rine, J.; Miller, J.L.; Walker, D. Catalytic hydrothermal conversion of
triglycerides to non-ester biofuels. Energy Fuel 2010, 24, 1305–1315.
15. Charusiri, W.; Vitidsant, T. Catalytic cracking of used cooking oil to liquid fuels over HZSM-5.
J. Energy 2003, 5, 58–68.
Catalysts 2012, 2
189
16. Melero, J.A.; Clavero, M.M.; Calleja, G.; Garcia, A.; Miravalles, R.; Galindo, T. Production of
biofuels via the catalytic cracking of mixtures of crude vegetable oils and nonedible animal fats
with vacuum gas oil. Energy Fuel 2010, 24, 707–717.
17. Maki-Arvela, P.; Kubickova, I.; Snare, M.; Eranen, K.; Murzin, D.Y. Catalytic deoxygenation of
fatty acids and their derivatives. Energy Fuel 2007, 21, 30–41.
18. Maki-Arvela, P.; Rozmyszowicz, B.; Lestari, S.; Simakova, O.; Eranen, K.; Salmi, T.; Murzin, D.Y.
Catalytic deoxygenation of tall oil fatty acid over palladium supported on mesoporous carbon.
Energy Fuel 2011, 25, 2815–2825.
19. Murata, K.; Liu, Y.; Inaba, M.; Takahara, I. Production of synthetic diesel by hydrotreatment of
Jatropha oils using Pt-Re/H-ZSM-5 catalyst. Energy Fuel 2010, 24, 2404–2409.
20. Wildschut, J.; Mahfud, F.H.; Venderbosch, R.H.; Heeres, H.J. Hydrotreatment of fast pyrolysis oil
using heterogeneous nobel-metal catalysts. Ind. Eng. Chem. Res. 2009, 48, 10324–10334.
21. Sotelo-Boyás, R.; Liu, Y.; Minowa, T. Renewable diesel production from the hydrotreating of
rapeseed oil with Pt/Zeolite and NiMo/Al2O3 catalysts. Ind. Eng. Chem. Res. 2011, 50, 2791–2799.
22. Huber, G.W.; O’Connor, P.; Corma, A. Processing biomass in conventional oil refineries:
Production of high quality diesel by hydrotreating vegetable oils in heavy vacuum oil mixture.
Appl. Catal. A 2007, 329, 120–129.
23. Liu, Y.; Sotelo-Boyás, R.; Murata, K.; Minowa, T.; Sakanishi, K. Hydrotreatment of Jatropha oil
to produce green diesel over trifunctional Ni-Mo/SiO2-Al2O3 catalyst. Chem. Lett. 2009, 38,
552–553.
24. Liu, Y.; Sotelo-Boyás, R.; Murata, K.; Minowa, T.; Sakanishi, K. Hydrotreatment of vegetable
oils to produce bio-hydrogenated diesel and liquefied petroleum gas fuel over catalysts containing
sulfided Ni-Mo and olid acids. Energy Fuel 2011, 25, 4675–4685.
25. Nagai, M.; Koizumi, K.; Omi, S. NH3-TPD and XPS studies of Ru/Al2O3 catalyst and HDS
activity. Catal. Today 1997, 35, 393–405.
26. Mott, C.J.B. Clay minerals―An introduction. Catal. Today 1988, 2, 199–208.
27. Kloprogge, J.T. Synthesis of smectites and porous pillared clay catalysts: A review. J. Porous
Mater. 1998, 5, 5–41.
28. Martinez-Oritz, M.J.; Fetter, G.; Dominguez; J.M.; Melo-Banda; J.A.; Ramos-Gomez, R.
Catalytic hydrotreating of heavy vacuum gas oil on Al- and Ti-pillared clays prepared by
conventional and microwave irradiation methods. Micropor. Mesopor. Mater. 2003, 58, 73–80.
29. Liu, Y.; Murata, K.; Okabe, K.; Inaba, M.; Takahara, I.; Hanaoka, T.; Sakanishi, K. Selective
hydrocracking of Fischer-Tropsch waxes to high-quality diesel fuel over Pt-promoted
polyoxocation-pillared montmorillonites. Top. Catal. 2009, 52, 597–608.
30. Bunch, A.Y.; Wang, X.; Ozkan, U.S. Hydrodeoxygenation of benzofuran over sulfided and
reduced Ni-Mo/γ-Al2O3 catalyst: Effect of H2S. J. Mol. Catal. A 2007, 270, 264–272.
31. Kloprogge, J.T.; Welters, W.J.J.; Booy, E.; de Beer, V.H.J.; van Santen, R.A.; Geus, J.W.;
Jansen, J.B.H. Catalytic activity of nickel sulfide catalysts supported on Al-pillared montmorillonite
for thiophene hydrodesulfurization. Appl. Catal. A 1993, 97, 77–85.
32. Iranmahboob, J.; Toghiani, H.; Hill, D.O. Dispersion of alkali on the surface of Co-MoS2/clay
catalyst: A comparison of K and Cs as a promoter for synthesis alcohol. Appl. Catal. A 2003, 247,
207–218.
Catalysts 2012, 2
190
33. Liu, Y.; Murata, K.; Hanaoka, T.; Inaba, M.; Sakanishi, K. Syntheses of new
peroxo-polyoxometalates intercalated layered double hydroxides for propene epoxidation by
molecular oxygen in methanol. J. Catal. 2007, 248, 277–287.
34. Liu, Y.; Murata, K.; Sakanishi, K. Hydroisomerization-cracking of gasoline distillate from
Fischer–Tropsch synthesis over bifunctional catalysts containing Pt and heteropolyacids. Fuel
2011, 90, 3056–3065.
35. Liu, Y.; Koyano, G.; Misono, M. Hydroisomerization of n-hexane and n-heptane over
platinum-promoted Cs2.5H0.5PW12O40 (Cs2.5) studied in comparison with several other solid acids.
Top. Catal. 2000, 11, 239–246.
36. Liu, Y.; Na, K.; Misono, M. Skeletal isomerization of n-pentane over Pt-promoted cesium
hydrogen salts of 12-tungstophosphoric acid. J. Mol. Catal. A 1999, 141, 145–153.
37. Liu, Y.; Misono, M. Hydroisomerization of n-butane over platinum-promoted cesium hydrogen
salt of 12-tungstophosphoric acid. Materials 2009, 2, 2319–2336.
© 2012 by the authors; licensee MDPI, Basel, Switzerland. This article is an open access article
distributed under the terms and conditions of the Creative Commons Attribution license
(http://creativecommons.org/licenses/by/3.0/).